Página 157
... single crystal ) . 192 Tin ( two orientations of single crystal ) . 193 Antimony ( two orientations of single crystal ) . Bismuth .. 195 196 Tellurium ( two orientations of single crystal ) . Summary . 200 202 INTRODUCTION The pressure ...
... single crystal ) . 192 Tin ( two orientations of single crystal ) . 193 Antimony ( two orientations of single crystal ) . Bismuth .. 195 196 Tellurium ( two orientations of single crystal ) . Summary . 200 202 INTRODUCTION The pressure ...
Página 166
... single excursion to 30,000 . Solenhofen limestone , which was , perhaps , first suggested at the Geophysical ... single substance at 30 ° and 75 ° with a single set - up . Even as it was , the two runs were often not complete . Attempts ...
... single excursion to 30,000 . Solenhofen limestone , which was , perhaps , first suggested at the Geophysical ... single substance at 30 ° and 75 ° with a single set - up . Even as it was , the two runs were often not complete . Attempts ...
Página 203
... Single crystal tin in two orientations decreases smoothly in resistance over the entire range , with practically no change in the ratio of resistance in different directions . Single crystal antimony is the only known example of a metal ...
... Single crystal tin in two orientations decreases smoothly in resistance over the entire range , with practically no change in the ratio of resistance in different directions . Single crystal antimony is the only known example of a metal ...
Contenido
Polymorphic Transitions of 35 Substances to 50000 | 44 |
POLYMORPHIC TRANSITIONS OF 35 SUBSTANCES TO 50000 Kgcm² Received December 10 1936 Presented December 9 1936 | 46 |
Detailed Data | 63 |
Otras 29 secciones no mostradas
Otras ediciones - Ver todas
Términos y frases comunes
Academy American atmospheric pressure Boston Brookline caesium Cambridge Cambridge carboloy cent Centigrade temperature change of volume chap Charles chemistry cm/gm gm cal/gm cm³/gm cm³/gm kg cm/gm coefficient Committee compressibility constantan copper curvature cylinder decreasing pressure dogfish effect elasmobranch electrical Elihu Thomson experimental external pressure extrapolation Foreign Honorary Members friction galvanometer Guanidine Harvard Henry ice point cell II-III inches increasing and decreasing IODOACETIC ACID junctions kg cm/gm gm kg/cm² Latent Heat low pressure lower manganin material maximum means melanophore metal Mustelus obtained P. W. Bridgman phase diagram plate plug polymorphic Postulates pressure in thousands pressure range Pressure Temperature Professor pups resistance Righi-Leduc effects room temperature rubidium Sciences Section shearing curve shearing strength shown in Figure sluggish steel stopper substance temperature against pressure theorem thousands of kg/cm² tion transition line transition parameters transition pressure University values volume apparatus volume change William wire York